In order to improve the comprehensive performance of permeable concrete，nano-silicon and polypropylene fiber were added to permeable concrete to study the performance of the composite modified permeable concrete.Firstly，the influence of single-doped nano-silicon on the performance of cement paste and permeable concrete was studied，and the content of nano-silicon and the optimal water-to-binder ratio were determined.On this basis，different proportions of polypropylene fiber were mixed，and the reasonable content of polypropylene fiber was determined.The results show that nano-silicon improves the porosity of permeable concrete and increases the optimal water-to-binder ratio.When the content of nano-silicon is 0.5%，and the water-to-binder ratio is 0.32，the compressive strength of permeable concrete is the highest.Based on this ratio，the maximum compressive strength can be obtained by adding 1.0 kg/m3 polypropylene fiber，and the compressive strength after 7 d and 28 d is increased by 29.9% and 42.2%，respectively.Adding 1.5 kg/m3 polypropylene fiber has the most significant effect in improving the frost resistance of permeable concrete.After 300 freeze-thaw cycles，the residual rate of compressive strength and flexural strength are 62% and 75%，respectively，which are far higher than 40% and 55% of single-doped nano-silicon.

Publication Date

7-30-2024

DOI

10.14048/j.issn.1671-2579.2024.04.012

First Page

97

Last Page

103

Submission Date

February 2025

Reference

[1]BRIGH T SINGH S ,MURUGAN M .Performance of carbon fibre-reinforced pervious concrete (CFRPC ) subjected to static ,cyclic and impact loads [J].International Journal of Pavement Engineering ,2022 ,23(9):3113 -3128 .
[2]ALIMOHAMMADI V , MAGHFOURI M ,NOURMOHAMMADI D ,et al .Stormwater runoff treatment using pervious concrete modified with various nanomaterials :A comprehensive review [J].Sustainability ,2021 ,13(15):8552 .
[3]李振发 .纳米偏高岭土对混凝土抗冻性能的影响研究[J].中外公路 ，2023 ,43（3） ：265-269.LI Zhenfa .Effect of nano-metakaolin on frost resistance of concrete [J].Journal of China & Foreign Highway ,2023，43(3):265-269.
[4]边旭辉，申爱琴，连城，等.基于灰关联理论的玄武岩纤维混凝土孔与抗冻性能相关性研究 [J].中外公路 ，2022 ,42（4） ：192-198.BIAN Xuhui ,SHEN Aiqin ,LIAN Cheng ,et al .Correlation study between pore structure and frost resistance of basalt fiber reinforced concrete based on grey correlation theory [J].Journal of China & Foreign Highway ,2022，42(4):192-198.
[5]MOHAMMED B S ,LIEW M S ,ALALOUL W S ,et al .Properties of nano-silica modified pervious concrete [J].Case Studies in Construction Materials ,2018 ,8:409-422.
[6]FENG P ,CHANG H L ,LIU X ,et al .The significance of dispersion of nano-SiO2 on early age hydration of cement pastes [J].Materials & Design ,2020 ,186:108320 .
[7]TARANGINI D ,SRAVANA P ,SRINIVASA RAO P .Effect of nano silica on frost resistance of pervious concrete [J].Materials Today :Proceedings ,2022 ,51:2185 -2189 .[8]TARANGINI D ,SRAVANA P ,SRINIVASA RAO P .Laboratory investigations on properties of Nanosilica Pervious concrete [J].IOP Conference Series :Earth and Environmental Science ,2022 ,982(1):012009 .
[9]TOGHROLI A ,MEHRABI P ,SHARIATI M ,et al .Evaluating the use of recycled concrete aggregate and pozzolanic additives in fiber-reinforced pervious concrete with industrial and recycled fibers [J].Construction and Building Materials ,2020 ,252:118997 .
[10]NHAT HO TRAN T ,PUTTIWONGRAK A ,PONGSOPHA P,et al .Microparticle filtration ability of pervious concrete mixed with recycled synthetic fibers [J].Construction and Building Materials ,2021 ,270:121807 .
[11]AKAND L ,YANG M J ,WANG X N .Effectiveness of chemical treatment on polypropylene fibers as reinforcement in pervious concrete [J].Construction and Building Materials ,2018 ,163:32-39.
[12]AL-HADITHI A I ,NOAMAN A T ,MOSLEH W K .Mechanical properties and impact behavior of PET fiber reinforced self-compacting concrete (SCC ) [J].Composite Structures ,2019 ,224:111021 .
[13]MASTALI M ,DALVAND A .Use of silica fume and recycled steel fibers in self-compacting concrete (SCC )[J].Construction and Building Materials ,2016 ,125:196-209.
[14]赵剑锋 ,杨晓杰 ,李好新 ,等.短切纤维对透水混凝土性能的影响 [J].建筑材料学报 ,2019 ,22(2):266-271.ZHAO Jianfeng ,YANG Xiaojie ,LI Haoxin ,et al .Effect of chopped fibers on the performance of pervious concrete [J].Journal of Building Materials ,2019 ,22(2):266-271.
[15]AKAND L ,YANG M J ,WANG X N .Effectiveness of chemical treatment on polypropylene fibers as reinforcement in pervious concrete [J].Construction and Building Materials ,2018 ,163:32-39.
[16]DAI Z ,LI H ,ZHAO W Z ,et al .Multi-modified effects of varying admixtures on the mechanical properties of pervious concrete based on optimum design of gradation and cement-aggregate ratio [J].Construction and Building Materials ,2020 ,233:117178 .
[17]郑木莲 .多孔混凝土排水基层研究 [D].西安 :长安大学 ,2004 .ZHENG Mulian .Study on porous concrete permeable base[D].Xi’an:Chang’an University ,2004 .
[18]赵苏 ,王金鹏 ,关达人 ,等.吸附法制备固态聚羧酸减水剂[J].混凝土 ,2018 (11):81-85.ZHAO Su ,WANG Jinpeng ,GUAN Daren ,et al .Preparation of solid polycarboxylate superplasticizer by adsorption [J].Concrete ,2018 (11):81-85.

Download

Share

COinS