Abstract

Polyurethane mixture is composed of polyurethane binder，rubber particles，and stones.Compared with ordinary asphalt mixture，it has the characteristics of a higher content of rubber particles and large void ratios.This article first tested the viscosity-time curve and viscosity-temperature curve of one-component polyurethane and determined the compaction temperature of the polyurethane mixture.Based on the rutting test，three-point bending test，water immersion Marshall test，freeze-thaw splitting test，and pendulum friction test，the road performance of the polyurethane mixture under different replacement amounts of rubber particles was tested.The research results show that the mixing temperature of PU- 1 polyurethane mixture can be basically controlled between 73 ℃ and 81 ℃，and it can be spread and rolled at room temperature （25 ℃）；the polyurethane mixture is cured after four days at room temperature.To accelerate the curing，the water spraying method can be used；under the condition of ensuring high temperature performance，when the replacement amount of rubber particles continues to increase，the maximum flexural strain，RMSR value，RTSR value，and BBPN value of the polyurethane mixture increase linearly.It shows that the rubber particles can promote low temperature performance，water stability，and slip resistance of the polyurethane mixture.

Publication Date

12-17-2024

DOI

10.14048/j.issn.1671-2579.2024.06.015

First Page

141

Last Page

147

Submission Date

February 2025

Reference

[1]LU G Y ,LIU P F ,WANG Y H ,et al .Development of a sustainable pervious pavement material using recycled ceramic aggregate and bio-based polyurethane binder [J].Journal of Cleaner Production ,2019 ,220: 1052 -1060 .
[2]SHEN D Y ,SHI S ,XU T ,et al .Development of shape memory polyurethane based sealant for concrete pavement[J].Construction and Building Materials ,2018 ,174: 474-483.
[3]LIU M ,HAN S ,SHANG W ,et al .New polyurethane modified coating for maintenance of asphalt pavement potholes in winter-rainy condition [J].Progress in Organic Coatings ,2019 ,133: 368-375.
[4]孙敏 ,郑木莲 ,毕玉峰 ,等.聚氨酯改性沥青改性机理和性能[J].交通运输工程学报 ,2019 ,19(2): 49-58. SUN Min ,ZHENG Mulian ,BI Yufeng ,et al .Modification mechanism and performance of polyurethane modified asphalt [J].Journal of Traffic and Transportation Engineering ,2019 ,19(2): 49-58.
[5]ZHANG H ,LIU Z ,MENG X .Noise reduction characteristics of asphalt pavement based on indoor simulation tests [J].Construction and Building Materials ,2019 ,215(10):285-297.
[6]LI W ,HUYAN J ,TIGHE S L ,et al .An innovative primary surface profile-based three-dimensional pavement distress data filtering approach for optical instruments and tilted pavement model-related noise reduction [J].Road Materials & Pavement Design ,2019 ,20(1):132-150.
[7]BAZMARA B ,TAHERSIMA M ,BEHRAVAN A .Retracted :Influence of thermoplastic polyurethane and synthesized polyurethane additive in performance of asphalt pavements [J].Construction and Building Materials ,2018 ,166:1-11.
[8]班午东 .橡胶颗粒沥青混合料的组成及性能研究 [D].重庆: 重庆交通大学 ,2011 .BAN Wudong .Study on composition and performance of granulated crumb rubber asphalt mixture [D].Chongqing : Chongqing Jiaotong University ,2011 .
[9]赵素艳 .橡胶沥青混合料路用性能及其温拌效果研究[D].长春 : 吉林大学 ,2014 .ZHAO Suyan .Research on pavement performance and warm mix effect of rubber modified asphalt mixture [D].Changchun : Jilin University ,2014 .
[10]张聪 .橡胶颗粒沥青路面耐久性研究 [D].西安 : 长安大学,2012 .ZHANG Cong .Study on durability of granulated crumb rubber asphalt pavement [D].Xi’an:Chang’an University ,2012 .
[11]孙晟凯 .聚氨酯混合料材料组成优化及服役性能研究[D].重庆 : 重庆交通大学 ,2021 .SUN Shengkai .Research on optimization of material composition and service performance of polyurethane mixture [D].Chongqing : Chongqing Jiaotong University ,2021 .
[12]VENNAPUSA P K R ,ZHANG Y ,WHITE D J .Comparison of pavement slab stabilization using cementitious grout and injected polyurethane foam (article ) [J].Journal of Performance of Constructed Facilities ,2016 ,30(6): 1-14
[13]仝玎朔 .聚氨酯弹性材料组成设计及路用性能研究 [D].西安 : 长安大学 ,2018 .TONG Dingshuo .Study on composition design and pavement performance of polyurethane elastic material [D].Xi’an: Chang’an University ,2018 .
[14]CHEN T ,MA T ,HUANG X M ,et al .The performance of hot-recycling asphalt binder containing crumb rubber modified asphalt based on physiochemical and rheological measurements [J].Construction and Building Materials ,2019 ,226: 83-93.
[15]王火明 ,李汝凯 ,王秀 ,等.多孔隙聚氨酯碎石混合料强度及路用性能 [J].中国公路学报 ,2014 ,27(10): 24-31.WANG Huoming ,LI Rukai ,WANG Xiu ,et al .Strength and road performance for porous polyurethane mixture [J].China Journal of Highway and Transport ,2014 ,27(10): 24-31.
[16]黎小顺 .聚氨酯混合料与沥青混合料路用性能评价对比[J].中外公路 ,2021 ,41(3): 304-309.LI Xiaoshun .Evaluation and comparison of road performance between polyurethane mixture and asphalt mixtures [J].Journal of China & Foreign Highway ,2021 ,41(3): 304-309.
[17]李添帅 ,陆国阳 ,王大为 ,等.高性能聚氨酯透水混合料关键性能研究 [J].中国公路学报 ,2019 ,32(4): 158-169.LI Tianshuai ,LU Guoyang ,WANG Dawei ,et al .Key properties of high-performance polyurethane bounded pervious mixture [J].China Journal of Highway and Transport ,2019 ,32(4): 158-169.
[18]金鑫 ,郭乃胜 ,尤占平 ,等.聚氨酯改性沥青研究现状及发展趋势 [J].材料导报 ,2019 ,33(21): 3686 -3694 .JIN Xin ,GUO Naisheng ,YOU Zhanping ,et al .Research and development trends of polyurethane modified asphalt[J].Materials Reports ,2019 ,33(21): 3686 -3694 .
[19]贾军红 ,刘大昌 .紫外光固化聚氨酯改性沥青及其混合料自愈合性能研究 [J].中外公路 ,2022 ,42(5): 241-245.JIA Junhong ,LIU Dachang .Study on the self-healing performance of UV cured polyurethane modified asphalt and its mixture [J].Journal of China & Foreign Highway ,2022 ,42(5):241-245.
[20]张长林 ,张丹 ,张勇强 ,等.路用水性聚氨酯改性环氧树脂的制备与工作性能 [J].中外公路 ,2022 ,42(1): 215-220.ZHANG Changlin ,ZHANG Dan ,ZHANG Yongqiang ,et al.Preparation and workability of waterborne polyurethane modified epoxy resin for road use [J].Journal of China & Foreign Highway ,2022 ,42(1):215-220.

Download

Share

COinS