Utilizing crushed waste glass as a substitute for natural aggregate in asphalt mixtures presents significant economic potential and environmental protection advantages. However, compared with natural aggregates, the low-strength glass aggregates are prone to crushing under load, necessitating an investigation into the crushing behavior of glass aggregates under load and its influence on the performance of asphalt mixture. In this paper, the crushing behavior of the mixture was analyzed through rotational compaction test and digital image processing technology, using the aggregate crushing index of the mixture as an indicator to evaluate its road performance. The results show that as the number of compaction times and the proportion of glass aggregates increase, the aggregate crushing index of the mixture rises, leading to more pronounced crushing phenomena in glass asphalt mixtures, primarily due to the crushing of glass aggregates. By extracting the void information from the cross-section of the glass asphalt mixture specimen, it is found that the void number and the void area in the mixture decrease with an increase in the number of compaction times and the proportion of glass aggregates. Within a certain range of glass content, the crushing behavior of glass aggregates significantly impacts the road performance and durability of the asphalt mixture, while having no noticeable effect on skid resistance. As the aggregate crushing index of the glass asphalt mixture increases, the high-temperature performance of the mixture deteriorates; when the crushing index is greater than 4.45%, its resistance to high-temperature deformation does not meet the specification requirements. Conversely, when the crushing index is below 3.25%, the low-temperature cracking resistance, water stability, and durability of the mixture are improved, but exceeding this threshold adversely affects the mixture's low-temperature cracking resistance, water stability, and durability. Therefore, it is suggested that the glass content in glass asphalt mixture should not exceed 20%, and the number of rotary compaction times should not exceed 150.

Publication Date

2-5-2026

DOI

10.14048/j.issn.1671-2579.2026.01.008

First Page

80

Last Page

89

Submission Date

February 2026

Reference

[1]中国物资再生协会.2024中国再生资源回收行业发展报告 [J].资源再生,2024 (7):27-38.China National Resources Recycling Association.2024 China renewable resource recycling industry development report [J].Resource Recycling,2024 (7):27-38.
[2]SUDHARSAN N,PALANISAMY T,YARAGAL S C,et al.Environmental sustainability of waste glass as a valuable construction material：A critical review (Review ) [J].Ecology,Environment and Conservation,2018,24:S331-S338.
[3]YUAN X H,WANG J B,SONG Q M,et al.Integrated assessment of economic benefits and environmental impact in waste glass closed-loop recycling for promoting glass circularity [J].Journal of Cleaner Production,2024,444:141155.
[4]白伟,孔维康,孟勇军.玻璃纤维改性沥青用于张力带的路面寿命和成本研究 [J].中外公路,2023,43(5):62-66.BAI Wei,KONG Weikang,MENG Yongjun.Study on pavement life and cost of glass fiber modified asphalt for tension belt [J].Journal of China & Foreign Highway,2023,43(5):62-66.
[5]SUN Z L,CHEN B W,LIU S,et al.Polyurethane modified asp halt mixture incorporating waste glass with a wide particle size range:Preparation and performance evaluation [J].Case Studies in Construction Materials,2024,20:e03119.
[6]张思成,盛冬发,罗志敏.玻璃沥青混合料的制备与路用性能研究 [J].公路,2021,66(6):11-16.ZHANG Sicheng,SHENG Dongfa,LUO Zhimin.Research on the preparation and road performance of glass asphalt mixture [J].Highway,2021,66(6):11-16.
[7]SU N,CHEN J S.Engineering properties of asphalt concrete made with recycled glass [J].Resources,Conservation and Recycling,2002,35(4):259-274.
[8]陈永志.废玻璃对排水沥青混合料路用性能影响研究[J].公路工程,2015,40(2):299-305.CHEN Yongzhi.Research of waste glass on the performance of drainage asphalt mixture [J].Highway Engineering,2015,40(2):299-305.
[9]ARABANI M.Effect of glass cullet on the improvement of the dynamic be haviour of asphalt concrete [J].Construction and Building Materials,2011,25:1181 -1195.
[10]袁峻,黄俊,王波,等.玻璃沥青混凝土阻热降温性能 [J].科学技术与工程,2021,21(32):13880 -13885.YUAN Jun,HUANG Jun,WANG Bo,et al.Thermal resistance and cooling performance of glass asphalt concrete [J].Science Technology and Engineering,2021,21(32):13880 -13885.
[11]袁峻,黄俊,王波,等.废旧玻璃沥青混凝土路用性能和导热性能研究 [J].沈阳建筑大学学报 (自然科学版 ),2021,37(3):502-509.YUAN Jun,HUANG Jun,WANG Bo,et al.Study on road performance and thermal conductivity of waste glass asphalt concrete [J].Journal of Shenyang Jianzhu University (Natural Science ),2021,37(3):502-509.
[12]DU Y F,DAI M X,DENG H B,et al.Incorporating hollow glass microsphere to cool asphalt pavement:Preliminary evaluation of asphalt mastic [J].Construction and Building Materials,2020,244:118380.
[13]LACHANCE-TREMBLAY É,PERRATON D,VAILLANCOURT M,et al.Degradation of asphalt mixtures with glass aggregates subjected to freeze-thaw cycles [J].Cold Regions Science and Technology,2017,141:8-15.
[14]赵晓宁.基于表面处理工艺的废旧玻璃沥青混合料路用性能研究 [D].重庆:重庆交通大学,2022.ZHAO Xiaoning.Study on road performance of waste glass asphalt mixture based on surface treatment technology [D].Chongqing:Chongqing Jiaotong University,2022.
[15]王浩博.废玻璃表面改性及其与沥青界面黏附性能影响研究 [D].重庆:重庆交通大学,2022.WANG Haobo.Study on surface modification of waste glass and its influence on interfacial adhesion with asphalt[D].Chongqing:Cho ngqi ng Jiaotong University,2022.
[16]LI C Q,WANG H B,FU C L,et al.Effect and mechanism of waste glass powder silane modification on water stability of asphalt mixture [J].Construction and Building Materials,2023,366:130086.
[17]ZHANG M,QIAN Z D,ZHOU Y D,et al.Test and evaluation for effects of aggregates fragmentation on performance of lightweight asphalt concrete [J].Construction and Building Materials,2018,169:215-222.
[18]王二兵,杜西江,徐良,等.再生集料破碎行为对沥青混合料性能影响 [J].公路工程,2021,46(2):77-81,102.WANG Erbing,DU Xijiang,XU Liang,et al.Effect of crushing behavior on the road performance of asphalt mixture containing recycled aggregate [J].Highway Engineering,2021,46(2):77-81,102.
[19]吴胜坤,朱文兵,周俊,等.多孔沥青混合料内粗集料破碎规律分析 [J].现代交通技术,2020,17(4):20-26.WU Shengkun,ZHU Wenbing,ZHOU Jun,et al.Analysis on crushing regulation of coarse aggregate in porous asphalt mixture [J].Modern Transportation Technology,2020,17(4):20-26.
[20]SHI L W,WANG D Y,XIAO X,et al.Meso-structural characteristics of asphalt mixture main skeleton based on meso-scale analysis [J].Construction and Building Materials,2020,232:117263.
[21]刘宇,张肖宁,迟凤霞.国外 SCB (半圆弯抗 )试验方法在沥青混合料中的研究与应用 [J].中外公路,2008,28(3):190-192.LIU Yu,ZHANG Xiaoning,CHI Fengxia.Research and application of SCB (semi-circular bending resistance ) test method in asphalt mixture abroad [J].Journal of China & Foreign Highway,2008,28(3):190-192.
[22]LI X L,LYU X C,ZHOU Y H,et al.Homogeneity evaluation of hot in-place recycling asphalt mixture using digital image processing technique [J].Journal of Cleaner Production,2020,258:120524.
[23]吕松涛,陈淇,鲁巍巍,等.沥青混合料低温半圆弯曲试验评价指标研究 [J].中外公路,2025,45(3):25-36.LYU Songtao,CHEN Qi,LU Weiwei,et al.Study on evaluation index of semi-circular bending test of asphalt mixture at low temperature [J].Journal of China & Foreign Highway,2025,45(3):25-36.
[24]ZHOU B C,ZHANG J P,PEI J Z,et al.Design and evaluation of high-luminance porous asphalt mixtures based on wasted glass for sponge city [J].Construction and Building Materials,2021,273:121696.
[25]ALI ANWARI R,COSKUN S,SALTAN M.Research on recycle of waste fluorescent lamp glasses and use as mineral filler in asphalt mixture [J].Journal of Material Cycles and Waste Management,2023,25(1):258-271.
[26]NOURA S,YAGHOUBI E,FRAGOMENI S,et al.Fatigue and stiffness characteristics of asphalt mixtures made of recycled aggregates [J].International Journal of Fatigue,2023,174:107714.
[27]黄优,张允宝,刘朝晖,等.考虑正交异性的粒料压实特性及其结构力学行为研究 [J].中外公路,2024,44(5):117-124.HUANG You,ZHANG Yunbao,LIU Zhaohui,et al.Compaction characteristics of granular material and its structural mechanical behavior considering orthotropy [J].Journal of China & Foreign Highway,2024,44(5):117-124.

Download

Share

COinS